PPS FILTER BAG FABRIC
FABRIC QUALITY: PPS - DF 050 PPS
WEIGHT: 500 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 2.0 mm (DIN EN ISO 9073 – Part 2)
DENSITY: 0.21 g/cm3
AIR PERMEABILITY: 180 per minute l/(dm2 .min)(DIN 53887)
* 11.000 per hour – 14.000 l/(dm2 .hr) @ 200 Pa / 5 cm >
PPS FILTER BAG FABRIC
FABRIC QUALITY: PPS - DF 055 PPS
WEIGHT: 550 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 2.2 mm (DIN EN ISO 9073 – Part 2)
DENSITY: 0.22 g/cm3
AIR PERMEABILITY: 160 per minute l/(dm2 .min) (DIN 53887)
* 9,000 – 12,000 l/(dm2 .hr) @ 200 Pa
per hour
BREAKING STRENGTH: Transverse 175 kgf /5 cm Longitudinal 130 kgf /5 cm *(EXAMPLE SIZE 200/50 mm) DIN EN 29073 – Part 3
WORKING TEMPERATURE: 190-210 C
A POLISHING PROCESS, CALLED GAZE AND KALENDER, HAS BEEN PERFORMED ON THE FABRIC SURFACES.
PTFE IMPRINT PROCESS HAS BEEN APPLIED TO THE FABRIC, WHICH PROVIDES RESISTANCE AGAINST WATER AND OIL.
PPS THE FRONT AND BACK SIDES OF THE FABRIC ARE NEEDLED DOUBLE SIDED DURING NEEDLEING.
ALSO, INTERNAL TISSUE (SCRIM) HAS BEEN PLACED IN THE FABRIC, WHICH INCREASES ITS DURABILITY.