POLYESTER FILTER BAG FABRIC
FABRIC QUALITY: POLYESTER - DF 050 PE
WEIGHT: 500 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 1.8 mm (DIN EN ISO 9073 – Part 2)
DENSITY: 0.29 g/cm3
AIR PERMEATION: 200 l/(dm2 .min)(DIN 53887)
* 11,000 per hour – 14.000 l/(dm2 .hr) @ 200 Pa 5 cm
*(EXAMPLE MEASUREMENT 200/50 mm)DIN EN 29073 – Part 3
OPERATING TEMPERATURE: 150 C
POLYESTER FILTER BAG FABRIC
FABRIC QUALITY: POLYESTER - DF 055 PE
WEIGHT: 550 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 2.0 mm(DIN EN ISO 9073 – Part 2)
DENSITY: 0.29 g/cm3
AIR PERMEATION: 160 l/(dm2 .min)(DIN 53887)
* 9,000 per hour – 12,000 l/(dm2 .hr) @ 200 Pa
BREAKING STRENGTH: Transverse 165 kgf /5 cm Longitudinal 145 kgf /5 cm *(EXAMPLE 200/50 mm) DIN EN 29073 – Part 3
OPERATING TEMPERATURE: 150 C
THE POLISHING PROCESS, WHICH WE CALL GAZE AND KALENDER, HAS BEEN PERFORMED ON THE FABRIC SURFACES.
HYDROPHOBIC IMPRINT PROCESS HAS BEEN APPLIED TO THE FABRIC, PROVIDING RESISTANCE AGAINST WATER AND OIL.
FRONT AND BACK SIDES OF POLYESTER FABRIC DURING NEEDLEING. ÇNEEDED DOUBLE SIDED.
IT IS ALSO INTERNAL TO THE FABRIC WHICH INCREASES ITS DURABILITY. TISSUE (SCRIM) HAS BEEN PLACED.