FIBERGLASS FILTER BAG FABRIC
FABRIC QUALITY: GLASS FIBER - DF 055 FIBERGLASS
WEIGHT: 550 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 0.9 mm (DIN EN ISO 9073 – Part 2)
MINIMUM EXPLOSION RESISTANCE: 55 kg/cm2 === 5500 kPA
AIR PERMEABILITY: 30-50 resp. 15-45 l/ (dm2 .min) @ 200 PA
DUST SIZE: 10 mg/Nm3
BREAKING STRENGTH: Transverse 3000 N /5 cm Longitudinal 4000 N/5 cm *(EXAMPLE SIZE 200/ 50 mm) DIN EN 29073 – Part 3
OPERATING TEMPERATURE: 260-280 C
FIBERGLASS FILTER BAG FABRIC
FABRIC QUALITY: GLASS FIBER - DF 075 FIBERGLASS
WEIGHT: 750 g/m2 (DIN EN 29073 – Part 1)
THICKNESS: 1.1 mm (DIN EN ISO 9073 – Part 2)
MINIMUM EXPLOSION RESISTANCE: 55 kg/cm2 === 5500 kPA
AIR PERMEABILITY: 20-40 resp. 15-45 l/ (dm2 .min) @ 200 PA
DUST SIZE: 10 mg/Nm3
BREAKING STRENGTH: Transverse 3000 N /5 cm Longitudinal 4000 N/5 cm *(EXAMPLE SIZE 200/50 mm) DIN EN 29073 – Part 3
WORKING TEMPERATURE: 260-280 C
THE FABRIC IS COATED WITH A PTFE MEMBRANE MEMBRANE THAT PROVIDES RESISTANCE AGAINST WATER AND OIL.
THE DOUBLE BASE AND REINFORCEMENT OF THE FILTER BAGS WILL BE SEWED FROM PTFE FELT
EVERY POINT OF THE FILTER BAG WILL BE SEWED WITH PTFE SEWING THREAD.
FILTER BAGS ARE WARRANTY AGAINST DEFECTS IN MATERIALS AND WORKMANSHIP FOR 3 YEARS.